SSP 100 JOINT FILLER

                    SSP-100 IS A 100% SOLIDS PURE POLYUREA JOINT FILLER

MATERIAL WITH 300% ELONGATION AND 86 SHORE A HARDNESS. 

Application is by mechanical plural pump or 600ml side-by-side cartridges*.  It is used to fill concrete saw-cut joints, construction joints and random cracks in concrete floors.   SSP-100 is self-leveling during application.  It can be shaved flush in as little as 15-30 minutes after installation or the following day. It contains no urethane which makes the joint hard to shave after a few hours and also restricts elongation of the joint material.  It is also moisture tolerant and will not swell in the presence of moisture. SSP-100 is sold in pre-pigmented or unpigmented to be colored in the field using color packs. *SSP-100 Joint Filler is available in 600ml side by side cartridges 10 & 110 gallon kits.

Advantages of SSP-100

•     Meets USDA Requirements •     100%  Pure Polyurea  •     Rapid Applications & Set Times •     Cold Applications to Below  0° F                        •     Not Sensitive to Moisture •     Non-Flammable •     Excellent Abrasion Resistance •     High Impact Resistance •     Chemical Resistant

"Pure" vs. "Hybrid" Polyurea

It's the urethane in polyurea joint products that make the joints swell.Urethane are highly moisture intolerant. Urethane also reduces the tensile elongation in joint fillers. causing them to "zipper" or split from the sidewalls of the joint in a relatively short time after installation.  Urethane cures hard quickly and makes the joint much more difficult to shave after only a few hours.  SSP products contain no urethane.  It is 100% Pure Polyurea. Have you ever tried to shake a cartridge like they recommend to mix it?  It does lower the price though.

Download the Data Sheet

Download the White Paper

TECH DATA

General: Solids Content:                                     100% Shelf Life:                                               1 year  Hardness:  ASTM D2240           Shore A 85 +/- 5    Tensile:  ASTM D412                              > 600 psi Elongation:  ASTM D412                         > 300 % Tensile Modulus:  ASTM D412              > 600psi MIXING: Mix Ratio:                                                1:1    Pot life: (small quantity)                    3-4 min. Tack free time :                                     6-7 min.  CURE TIME: Light traffic:                          15 min. @70 deg. Full Traffic:                            60 min. @70 deg. Stand time in static mixer:                2-3 min